厂家(产地):伊朗石化 | 牌号:2100TN00 | 销售方式:品牌经销 |
类型:标准料 |
用途: 薄膜
重要参数: 熔体流动速率:0.3 g/10min 密度:0.921 g/cm3 拉伸强度:26 MPa 断裂伸长率:500 %
生产厂商:伊朗国家石化公司
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 熔体流动速率 | ISO 1133 | 0.3 | Dg/min | |
密度 | ISO 1183(A) | 921 | kg/m3 | ||
机械性能 | 冲击强度 | ASTM D-4272 | 35 | kJ/m | |
撕裂强度TD | ISO 6383-2 | 25 | KN/ m | ||
撕裂强度MD | ISO 6383-2 | 20 | KN/ m | ||
屈服应力TD | ISO R527-1 | 11 | MPa | ||
屈服应力MD | ISO R527-1 | 12 | MPa | ||
拉伸强度TD | ISO R527-1 | 26 | MPa | ||
拉伸强度MD | ISO R527-1 | 29 | MPa | ||
断裂伸长率TD | ISO R527-1 | >500 | % | ||
断裂伸长率MD | ISO R527-1 | >200 | % | ||
弹性模量TD | ISO R527-1 | 190 | MPa | ||
弹性模量MD | ISO R527-1 | 180 | MPa | ||
摩擦系数 | ASTM D-1894 | 0.7 | |||
光学性能 | 光泽度 | ASTM D-2457 | 39±5 | % | |
雾度 | ASTM D1003A | 15 | % | ||
透明度 | DSM METHOD | 56 | mV | ||
其他 | 抗氧化剂 | DSM METHOD | 600±60 | ppm |
Grade Name | MFR (190oC/2.16 Kg) | Density | Application | |
LH0030 | certificate | 0.3 | 0.921 | Heavy duty films, Shrink films, Construction films, Agricultural films
|
LH0050 | certificate | 0.5 |
| Carrier bags, Shrink films, Blow molding, Packaging of stuff
|
LH0075 | certificate | 0.75 | 0.925 | Carrier bags, Shrink films, Blow molding, Packaging of food stuffs.
|
LF0200 | certificate | 2 | 0.920 | General purpose bags, Low tension, Power cable, Injection molding
|
LS0085 | 0.85 | 0.921 | Thin shrink film
| |
LS0085/KJ | 0.85 | 0.921 | Shrink packaging applications
| |
LF0190 | 1.9 | 0.921 | Carrier Bags, shrink films , Blow molding , Packaging of stuff
| |
LF0250/KJ | 2.5 | 0.921 | Packaging films
| |
LT0470/KJ | 4.7 | 0.924 | Stiffer thin films for textile packaging
| |
2602TH00 | MFI (190/2.16) 1.9 | 0.926 | Film, under blankets and films for medical applications. It is used in combination with LLDPE in products like diaper
| |
1922T | MFI (190/2.16) 22
| 0.919 | It is used for applications that require a good balance between flow properties and mechanical properties e.g. toys, household articles, clamping lids.
| |
2004TC37 | MFI (190/2.16) 4.7
| 0.921 | It is used for very thin films requiring good optical properties for general packaging.
| |
2100TN00 | MFI (190/2.16) 0.3
| 0.921 | It is suitable for application in Shrink hoods, Industrial sacks, Heavy duty carrier bags and liners.
| |
2101TN47 | MFI (190/2.16) 0.85
| 0.921 | This grade enables high speed production of film without blocking.
| |
2102TX00 | MFI (190/2.16) 1.9
| 0.921 | It is used in wide range of widths and thicknesses e.g. for punches, bags, liners and lamination film.
| |
2404TC47 | MFI (190/2.16) 4.7
| 0.924 | It is used for very thin films requiring good optical properties for general packaging applications e.g. covering film with very low blocking endency.
| |
2501TN00 | MFI (190/2.16) 0.75
| 0.925 | It is used in diaper film, lamination film and in applications where low blocking behavior without the help of additives is required.
|
低密度聚乙烯按聚合方法,可分为高压法和低压法。按照反应器类型可分为釜式法和管式法。以乙烯为原料,送入反应器,在引发剂的作用下以高压压缩进行聚合反应,从反应器出来的物料,经分离器除去未反应的乙烯之后,经熔融挤出造粒,干燥、掺合,送去包装。
LDPE和LLDPE都具有极好的流变性或熔融流动性。LLDPE有更小的剪切敏感性,因为它具有窄分子量分布和短支链。
在剪切过程中(例如挤塑),LLDPE保持了更大的粘度,因而比相同熔融指数的LDPE难于加工。在挤塑中,LLDPE***的剪切敏感性使聚合物分子链的应力松弛更快,并且由此物理性质对吹胀比改变的敏感性减小。
在熔体延伸中,LLDPE在各种应变速率下通常都具有较低的粘度。也就是说它将不会象LDPE一样在拉伸时产生应变硬化。随聚乙烯的形变率增加.LDPE显示出粘度的惊人增加,这是由低密度聚乙烯应用分子链缠结引起。
这种现象在 LLDPE中观察不出,因为在LLDPE中缺少长支链使聚合物不缠结。这种性能对薄膜应用极重要.因为 LLDPE薄膜在保持高强度和韧性下召易制更薄薄膜。nLLDPE的流变性可概括为“剪切时刚性”和“延伸时柔软”。
当用LLDPE 替代LDPE时薄膜挤塑设备和条件必须做修改。LLDPE的高粘度要求挤塑机有更大的功率.并提供更高的熔体温度和压力。
模口隙距必须加宽以避免由于产生高背压和熔体断裂而降低产量。LDPE和 LLDPE的一般模口隙距尺寸分别是O. 024~0. 040 in.和 0. 060-0. 10in。
LLDPE的“延伸时柔软”的特性在吹膜过程中是一个缺点。LLDPE的吹塑薄膜膜泡不象 LDPE的那么稳定。
一般的单唇风环对 LDPE的稳定足够使用.LLDPE的***的膜泡要求更完善的双唇风环来稳定。用双唇风环冷却内部膜泡可增加膜泡稳定性,同时在高生产率下提高薄膜生产能力。除了膜泡的更好冷却外,很多薄膜生产厂采用与LDPE共混方法以增强LLDPE溶道理上,LLDPE的挤塑可以在现有LDPE薄膜设备上完成,当LDPE的共混物中 LLDPE的浓度达 50%时。加工 *** LLDPE或富含 LLDPE的与LDPE共混材料时,采用一般的LDPE挤塑机,必需改进设备。
根据挤塑机的寿命,要求改进的可能是加宽模口隙距,改良风环,修改螺杆设计以更好挤出,必要时应增加电机功率和转矩。对于注塑应用,一般不需改进设备,但加工条件需达化。
滚塑加工要求LLDPE研磨成均匀颗粒(35筛孔)。加工过程包括用粉末状LLDPE填满模具,加热并双轴向地旋转模具使LLDPE均匀分布。冷却后产品从模具中移出。
1、物流运费说明
店铺报价不含运费,运费由买家承担,拍下付款后,买家可自行安排自己熟悉的物流上门提货,也可由卖家安排物流,运费提付(货送到后运费直接付给物流即可)。根据到货地址远近,及数量的多少,则运费不同。要货数量越多,运费越便宜。
2、在线下单
因塑胶行情价格波动较大,请用旺旺客服或电话直接询价确认后再拍。
3、在线支付
因塑胶行情价格波动较大,请拍下后当天内付款,不然不得不关闭交易喽~请体谅~
4、退换货政策
到货后请买家仔细确认货物完好后再签收,否则如无质量问题,不退不换哦~
5、发票制度说明
本店既可以线下交易也可线上支付交易,已设置默认绑定的是公司账户支付宝,也可换绑私人卡支付宝,请拍前联系旺旺确认账户后再拍,谢谢啦~